Epoxy-resin Composite Materials

YQXPOLYMER Epoxy resin for Composite Materials, consisting of Bisphenol-A Liquid Epoxy Resin, Bisphenol-A Semi-solid Epoxy Resin, Bisphenol-A Solid Epoxy Resin, Vacuum Infusion Process Solutions, and Water Treatment Pipeline Solutions, exhibits wettability with reinforcing materials, suitable for a variety of molding processes, high mechanical strength, impact resistance, high toughness, anti-cracking, corrosion resistance; whose are comprehensively applicable into wind power blades, aircraft wings, chemical pipelines, large storage tanks, acid and alkaline pools, brewing tanks, automotive components, surfboards, construction repair, etc.

Bisphenol-A Liquid Epoxy Resin 0161

Key Properties

  • Low viscosity, excellent wettability.
  • Low heat release peak, relatively long operation time.
  • Epoxy products leading in physical & mechanical performances, and fatigue resistance

Key Applications

  • Wind power blades
  • Chemical pipelines

Bisphenol-A Liquid Epoxy Resin 0161 Grads

 

Epoxy (g/mol)

Viscosity (mPa.s)(25°C)

Color

Hydrolysable Chlorine(%)

0161

175~185

8000~11000

≤40

≤0.05

Bisphenol-A Liquid Epoxy Resin 0164

Key Properties

  • Excellent wettability with reinforcing material.
  • Epoxy products leading in mechanical strength, resistance to cracking.
  • Multiple manufacturing processes, meeting various customer requirements.
  • Packing variety: barrels, tanks or customization.

Key Applications

  • Automotive structural parts
  • Aircraft skin, wings
  • Surfboards

Bisphenol-A Liquid Epoxy Resin 0164 Grads

 

Epoxy (g/mol)

Viscosity (mPa.s)(25°C)

Color

Hydrolysable Chlorine(%)

Notes

0164

183~190

10000~14000

≤30

≤0.05

Standard type

0164C

184~195

10000~16000

≤40

≤02

Universal type

0164E

184~194

11000~15000

≤30

≤0.03

DIC Technology

0164G

184~190

11000~15000

≤20

≤0.02

Low color, low yellowing

Bisphenol-A Liquid Epoxy Resin 0174

Key Properties

  • Excellent resistance of corrosion & penetration.
  • Low curing shrinkage rate with less cracks.
  • Excellent adhesion and fiber wetting ability, high-grade mechanical strength.

Key Applications

  • Laminated boards
  • Chemical storage tanks
  • Aquarium

Bisphenol-A Liquid Epoxy Resin 0174 Grads

 

Epoxy (g/mol)

Color

Softening point(°C)

Notes

0174

210~230

≤40

14~23

Universal type

860L

210~240

≤2

14~23

DIC technology

Bisphenol-A Semi-solid Epoxy Resin 0177E

Key Properties

  • Excellent wettability with fiber.
  • Epoxy products leading in mechanical strength and anti-cracking.
  • Excellent dispersion performance, conducive to subsequent operations

Key Applications

  • Treatment agent for carbon fiber
  • Treatment agent for glass fiber

Bisphenol-A Semi-solid Epoxy Resin 0177E Grads

 

Epoxy (g/mol)

Amine value(mgKOH/g)

0177E

230~270

≤2

Bisphenol-A Liquid Epoxy Resin 0191 & 1050

Key Properties

  • Low color, high transparency.
  • Excellent wettability with fibers and pigments.
  • Epoxy products leading in mechanical strength, electrical performance.
  • Epoxy products leading in mechanical strength, electrical performance

Key Applications

  • Golf clubs
  • Fishing rods

Bisphenol-A Liquid Epoxy Resin 0191 & 1050 Grads

 

Epoxy (g/mol)

Softening point (°C)

Color (Gardner)

Notes

0191

450~560

66~76

≤1

 

1050

450~500

64~74

≤2

DIC technology

Vacuum Infusion Process Solutions 9201A/B

Key Properties

  • Low mixing viscosity, excellent fiber wettability.
  • Long operational time, low heat release.
  • Excellent mechanical properties and anti-cracking properties.
  • Especially suitable for vacuum infusion process.

Key Applications

  • Wind power blades
  • Automotive lightweight parts

Vacuum Infusion Process Solutions 9201A/B grade

 

Epoxy (g/mol)

Viscosity (mPa.s)(25°C)

Amine value

(mgKOH/g)

Mix ratio weight ratio

9201A

170~185

800~1500

100

9201B

10~80

400~600

30~33

YQXPOLYMER 9201A/B is a special epoxy resin curing agent system for megawatt wind turbine blades with long operating time, excellent mechanical strength and DNV certified. 9201A/B has low mixing viscosity, excellent fiber wettability, long gel time and operable time, low exothermic peak, and excellent comprehensive mechanical properties after curing.

9201AB EPOXY RESIN CURING SYSTEM TECHNICAL DATA SHEET

Water Treatment Pipeline Solutions 9318A/B

Key Properties

  • Low mixing viscosity, excellent fiber wettability.
  • Excellent adhesion, suitable for bonding PE, PP and other materials.
  • Excellent mechanical properties, anti-cracking performance. Especially suitable for wet winding molding process.

Key Applications

  • Seawater desalination processing piping
  • Household water purifier

Water Treatment Pipeline Solutions 9318A/B grade

 

Epoxy (g/mol)

Viscosity (mPa.s)(25°C)

Amine value

(mgKOH/g)

Mix ratio weight ratio

9318A

185~195

800~1800

100

9318B

100~400

200~400

35~45

YQXPOLYMER 9821A/B is a high toughness epoxy resin curing system for winding molding. 9821A resin is modified 0164 epoxy resin, and 9821B curing agent is modified liquid acid anhydride. It has low mixing viscosity, long pot life, easy operation, and meets the process performance requirements of composite winding molding (high temperature curing system).

9821AB HIGH TOUGHNESS AND MEDIUM TEMPERATURE RESISTANT EPOXY RESIN SYSTEM FOR WINDING MOLDING TECHNICAL DATA SHEET

YQXPOLYMER 9824A/B is a high toughness epoxy resin curing system for winding molding. It has low mixing viscosity, moderate pot life, good wettability to carbon fiber and glass fiber, excellent mechanical properties and heat resistance of the cured product, and high toughness and crack resistance (medium temperature curing system).

9824AB EPOXY RESIN SYSTEM FOR WINDING MOLDING TECHNICAL DATA SHEET

More information or free samples or price quotations, please contact us via email: sales@yqxpolymer.com, or voice to us at: +86-28-8411-1861.

Some pictures and texts are reproduced from the Internet, and the copyright belongs to the original author. If there is any infringement, please contact us to delete.

Scroll to Top
Scroll to Top