Covalent adaptable networks (CANs) combine the uniqueness of thermoplastics and thermosets to allow for reprocessability while being covalently crosslinked. However, it is highly desirable but rarely achieved for CANs to simultaneously demonstrate reversibility and mechanical robustness. Herein, we report a feasible strategy to develop a novel epoxy vitrimer (EV) composed of adaptable phosphate networks (APNs), by which the EVs exhibit promising mechanical properties (tensile strength of 62.5 ~ 87.8 MPa and tensile modulus of 1360.1 ~ 2975.3 MPa) under ambient conditions.
At elevated temperatures, the topology rearrangement occurs relied on phosphate transesterification, which contributes to the shape memory performance, self-healing, reprocessing, and welding behaviors. Moreover, the incorporation of APNs allows for improvements in anti-ignition and also the inhibition of both heat release and smoke generation to avoid empress, asphyxiation, and toxication during burning, showing expected intrinsic fire safety. Thermal, mechanical properties, and flame retardancy of the reprocessed EVs after hot pressing are very close to those of the original EVs, which is attributed to the sufficient reversibility of APNs. Accordingly, combining the aforementioned features, EVs are manufactured as flame-triggered switches for fire alarms, which symbolizes the innovative development of high-performance covalent adaptable polymeric materials.
YQXPOLYMER cited from 王玉忠院士/陈力教授团队在含“宽温域”动态磷酸酯网络的火安全环氧树脂方面取得新进展-四川大学化学学院 (scu.edu.cn)
More information about epoxy resin, please contact us via email: sales@yqxpolymer.com, or voice to us at: +86-28-8411-1861.
Some pictures and texts are reproduced from the Internet, and the copyright belongs to the original author. If there is any infringement, please contact us to delete.